H13 po'latdan yasalgan novda

Material: Qotishma asboblar po'lati dumaloq bar H13
Jarayon: EAF plus LF plus VD plus Soxta va issiqlik bilan ishlov berish (ixtiyoriy)
Issiqlik bilan ishlov berish: normallashtirilgan / tavlangan / o'chirilgan / temperli

So'rov yuborish

Mahsulotni tanishtirish

Texnik xususiyatlari
Material	Qotishma asboblar po'lati dumaloq bar H13	Dumaloq bar	Dia (mm)	Maksimal 500
Jarayon	EAF plus LF plus VD plus Soxta va issiqlik bilan ishlov berish (ixtiyoriy)	Uzunlik (mm)	Maks 5800
Issiqlik Davolash	Normallashtirilgan / Tavlangan / Söndürülmüş / temperli	Plitalar paneli	Qalinligi (mm)	Maksimal 400
Yetkazib berish Vaziyat	Issiq zarb qilingan va qo'pol ishlov berilgan (Q/T dan keyin qora sirt) va burilgan (ixtiyoriy)	Kengligi (mm)	Maks 800
Sinov	SEP 1921-84 D/d ga muvofiq ultratovush tekshiruvi	Uzunlik (mm)	Maksimal 5800

Baho	C	Si	Mn	P	S	Cr	Mo	V
H13	0.32-0.45	0.80-1.20	0.20-0.50	0.030 dan kichik yoki unga teng	0.030 dan kichik yoki unga teng	4.75-5.50	1.10-1.75	0.80-1.20
4Cr5MoSiV1	0.33-0.43	0.80-1.20	0.20-0.50	0.030 dan kichik yoki unga teng	0.030 dan kichik yoki unga teng	4.75-5.50	1.10-1.60	0.80-1.20
1.2344	0.33-0.41	0.80-1.20	0.25-0.50	0.030 dan kichik yoki unga teng	0.020 dan kichik yoki unga teng	4.80-5.50	1.10-1.50	0.30-0.50
SKD61	0.35~0.42	0.80-1.20	0.25-0.50	0.030 dan kichik yoki unga teng	0.020 dan kichik yoki unga teng	4.80-5.50	1.00-1.50	0.80-1.15

H13 po'lati eng ko'p ishlatiladigan va vakillik issiq ishlaydigan po'latdir. Uning asosiy xususiyatlari quyidagilardir:

(1) U yuqori qattiqlik va yuqori qattiqlikka ega.

(2) Termal yorilishga mukammal qarshilik, suvni sovutish ish joyida ishlatilishi mumkin.

(3) O'rtacha aşınma qarshilik bilan, karbürleme yoki nitridlash ham sirt qattiqligini oshirish uchun ishlatilishi mumkin, ammo termal yorilish qarshiligi biroz kamayishi kerak.

(4) Uglerod miqdori past bo'lganligi sababli, ishlov berish paytida ikkilamchi qotib qolish qobiliyati yomon.

(5) U yuqori haroratda yumshatishga qarshilik ko'rsatish qobiliyatiga ega, ammo foydalanish harorati 540 darajadan (1000 daraja F) yuqori bo'lsa, qattiqlik tezda pasayadi (ya'ni, ish harorati 540 daraja).

(6) Issiqlik bilan ishlov berishning deformatsiyasi kichik.

(7) O'rta va yuqori ishlov berish qobiliyati.

(8) Dekarburizatsiyaga o'rtacha qarshilik.

Ilova